Materials Testing Fixtures is our core business. In structural engineering sector has continuously looking for materials that exhibit low densities and at the same time good strength, good stiffness, good abrasion behavior and impact, and are not easily susceptible to corrosion. The knowledge of the mechanical and physical characteristics of a material is the first step for a correct evaluation of the performance of the exercise component.
In research and development are frequently required materials testing fixture for the execution of tests that are not the standard kit for testing machines.
The standard equipment marketed, in accordance with regulations UNI, EN, ISO, ASTM, DIN, BS, AF, are made Carbon Steel , Stainless steel or metal alloys (nickel alloys) so as to give the product high performance, even at high temperatures and minimize side effects such as corrosion and oxidation in normal ambient laboratory conditions.
We produce a wide range of test equipment for the testing of materials made in accordance with standard devices and the customer specifications.
BOND TESTS
01
This test method covers the determination of the relative peel resistance of adhesive bonds between one rigid adherend and one flexible adherend when tested under specified conditions of preparation and testing. Usually the thickness of the sheets is shown in material specification. If the thickness is not stated, the flexible ...
02
This fixture is designed to maintain a constant peel angle of 90 degrees, as an upper sheet is peeled from the rest of a honeycomb panel. Using this fixture can be tested other structures consisting of a flexible face sheet and a more rigid substrate. Are recommended face sheet thicknesses ...
03
This test method can be used to determine the adhesive bond shear strength between other adherends as well. The basic testing principle is similar to that of the ASTM D 4501 Block-Shear Test Method.The standard specimen consists of two blocks, each 1.75” high and 2” wide, bonded together with a ...
04
This test method describes a procedure and fixture used to determine shear strengths of adhesives used to bond materials with moduli higher than the modulus of the adhesive. The size and shape of the specimens are variable within the physical restraints of the fixture.Two blocks of specific sizes are bonded ...
05
This testing device is used to determine the shear strength of the welds of welded wire fabric.As it regards the two standards ASTM A 497 and ASTM A 185, there are no substantial differences, for this reason they use the same test fixture. From the wire fabric, is cut a ...
06
ASTM D1781 Testing Fixture This procedure is useful for the determination of the peel resistance of adhesive bonds adhering a relatively flexible and adhering rigid; and the relatively flexible coating of a sandwich structure and its nucleus, to the test under the specified conditions. This standard does not purport to ...
COMPRESSION LOADING
01
The edgewise compressive strength of short sandwich construction specimens shall determine the load-carrying capacity of the construction in terms of developed facing stress. This is a standard method of obtaining sandwich edgewise compressive strengths for panel design properties, material specifications, research and development applications, and quality assurance. The request of ...
02
The fixture is used for testing composite materials under uniaxial compression. The flat piece is a load plate made of hardened steel, to be interposed between the upper protrusion of the specimen and the load floor of the test machine, to protect the load plate. There is actually no ASTM ...
03
It can be provided platens of all types, in all sizes and load capacities, and also custom designs for special applications. Platens of 6" diameter are the most popular size. Typically, platens are fabricated of fully through-heat-treated 440C stainless steel, characterized by high surface hardness and durability in combination with ...
This test method has the purpose of determining the mechanical properties of unreinforced and reinforced rigid plastics, including high-modulus composites, when loaded in compression at relatively low uniform rates of straining or loading. The test specimens employed are characterized of a standard shape. This fixture is used in order to test composite ...
05
This method defines the compression properties in the plane of composite materials with polymer matrix reinforced with high modulus fibers. The composite material forms are limited to continuous or discontinuous fiber-reinforced composites. For this reason, the elastic properties are particularly orthotropic with respect to the test direction. This test procedure ...
06
ASTM D6641 Testing Fixture This test method indicates the compression properties of strength and stiffness of composite materials with polymer matrix by means of a combined compression load. This type of testing can be applied to general composites that are balanced and symmetric. The specimen may be untabbed (Procedure A) ...
FASTENER RELATED TESTS
ASTM E399 TESTING FIXTURE Can be designed and fabricated clevises of all types and sizes . A typical pair of clevises are those conforming to ASTM Standard E 399. These forks are made of high-strength, heat-treated steel for tools, according to the ASTM standards. Exist three pair of tensile clevises ...
02
This test method is used for pull-through strength, i.e., the strength of the plates the fastener is holding together. The test specimen consists of two 1.5” square plates connected at their centers by the desired fastener being tested. To maintain proper rotational alignment of the two halves of the fixture ...
ASTM D953 TESTING FIXTURE This procedure is used for determining the bearing capacity of rigid plastic or in the form of sheets, printed form, or in the form thermoset pultruded. There are two procedures. Procedure A is applicable for the load voltage and Procedure B for the compression load. This ...
04
The bearing strength of a 1.5” wide test specimen assembly containing one or two ¼” diameter fasteners is to be determined.
05
ASTM Standard D 5961 includes four distinct laminate bearing test methods, identified as Procedures A, B, C, and D. Procedure B is actually a specimen support fixture. The other three procedures, as will be described here, are pin bearing fixtures. PROCEDURE A: DOUBLE-SHEAR TENSILE LOADING Procedure A in ASTM ...
FLEXURAL LOADING
ASTM F394 TESTING FIXTURE A ring supports thin circular disks of a monolithic ceramic material, or a whisker- or particle-reinforced ceramic matrix composite. These disks are loaded by a smaller diameter concentric ring, a so-called ring-on-ring loading. Thickness and material of the sample determine the required diameter of the support ...
02
ASTM D7249 Testing Fixture This is a specialized version of the standard Long Beam Flexure Fixture and includes linear bearings alignment rods. It does not have an adjustable structure, as it has been designed for specific load and support spans. In test environments such as the control of production quality, ...
03
This method is used for the resistance to the bending test for the ceramic is mainly governed by ASTM C 1161. This particular ASTM standard defines specific exemplary dimensions, corresponding to a choice of three support spans, ie., 20, 40 or 80 mm, called Configurations A, B, and C, respectively. ...
ASTM D790 Testing Fixture ASTM D790 are used for determining the flexural properties of unreinforced and reinforced plastics, including high modulus composites and electrical insulating materials utilizing a three-point loading system to apply a load to a simply supported beam (specimen). ASTM D790 can generally be applied to both rigid ...
ASTM D7264 Testing Fixture This test method determines the flexural properties (including strength, stiffness, and load/deflection behavior) of polymer matrix composite materials under the conditions defined. Procedure A is used for three-point loading and Procedure B is used for four-point loading. Procedure A—A three-point loading system utilizing center loading on ...
ASTM D393 Testing Fixture This test method covers the determination of the properties of flat sandwich constructions subjected to flatwise flexure in which the applied moments cause curvature of the sandwich facing planes. These tests may be conducted to determine the sandwich flexural stiffness, the core shear strength and shear ...
FRACTURE TOUGHNESS TESTS
ASTM D 6671 is used for determining the interlaminar fracture toughness of continuous fiber-reinforced composite materials. It can also be used in the adhesive joints testing. This test method is designed for use of composites consisting of unidirectional carbon fiber tape laminates with brittle and tough single-phase polymer matrices. An ...
02
This test apparatus is useful to determine the opening Mode I interlaminar fracture toughness, GIc, of continuous fiber-reinforced composite materials by the double cantilever beam specimen. This test application is employable with composites consisting of unidirectional carbon fiber and glass fiber tape laminates with brittle and tough single-phase polymer matrices. …
RUBBER TESTS
ASTM D395 Testing Fixture This test methods is useful for the test of rubber that should be used in applications in which the rubber will be subjected to compressive stresses in air or liquid media. For example in machinery mountings, vibration dampers, and seals. Two test methods are provided and ...
SHEAR LOADING
Shear Test Fixtures are designed for in-plane or interlaminar shear testing of composite materials. The V-Notched Beam Method, or more commonly known as the Iosipescu Shear Method, was standardized into ASTM D5379 in 1993, while the V-Notched Rail Shear Method was more recently introduced in 2005 under ASTM D7078. Both ...
ASTM D732 Testing Fixture ASTM D 732, defines a punch-type of shear test. This test method covers the procedure for determining the shear strength of composite materials in the form of sheets, plates, and molded shapes. The thicknesses of specimen can range from 0.050” to 0.500”. A disc from 1” diameter will ...
This system establishes the short-beam strength of reinforced composite materials with high modulus. The specimen is a short beam machined from a curve or a plate rolled up to 6,00 mm [0.25 in.] thick. The beam is loaded in three-point bending. Application of this test method is limited to continuous- ...
04
ASTM D4255-A Testing Fixture This test method indicates the cutting properties in the plane of a high modulus fiber-reinforced composite materials by two procedures. As regards the procedure A, laminates stuck between two pairs of loading rails are tested. When the tension load is applied to the rails, shear forces ...
This test method indicates the cutting properties in the plane of a high modulus fiber-reinforced composite materials by two procedures. As regards the procedure A, laminates stuck between two pairs of loading rails are tested. When the tension load is applied to the rails, shear forces arise in the specimen. ...
06
This fixtures has been designed for in-plane or interlaminar shear testing of composite materials. The V-Notched Beam Method, better known as Iosipescu Shear Method, was standardized into ASTM D5379 in 1993. For this test method V-notches specimen design is used in order to create a localized and approximate uniform shear ...
07
A sandwich panel or the core material itself can be tested in shear parallel to the flatwise plane. The fixture can be used to apply either a tensile or a compressive loading, although a tensile loading is most commonly utilized in order to eliminate buckling as a potential failure mode. ...
SPECIALTY COMPRESSION TEST FIXTURES
01
This type of NASA compression after impact (CAI) of compression of the test device is an alternative to the more popular Boeing compression after the compression of the device of the impact test. The NASA devices are 10 " long and 5" in width. As in Boeing method, a quasi-isotropic ...
02
The untabbed sample is 3 "long, 1" wide, and the thickness can vary depending on the material and layup in the testing phase. Northrop Specification recommended thicknesses from 0.125 "to 0.250". The standard sample contains a central "diameter hole 0.25, even if the unit has proved effective, even for compression ...
03
This common method in aerospace concerns compression tests on plates, rolled experimentation multidirectionaldetermination of the post-impact compressive strength. The methodis also useful for the compression tests after impact on composite materials, the company has acquired a new realization of controlled impact machine. The impact receiving sample is placed in the ...
ASTM D6484 Testing Fixture This test method is designed to produce notched compressive strength data for structural design allowables, material specifications, research and development, and quality assurance. Factors that influence the notched compressive strength and shall therefore be reported include the following: material, methods of material fabrication, accuracy of lay-up, ...
05
Knowledge of the damage resistance and damage tolerance properties of a laminated composite plate is useful for product development and material selection. The residual resistance data obtained by this test method will be used in the specification of materials and research and development. The properties obtained using this method will …
SPECIALTY TENSILE TESTS
01
This test method, performs a through-the-thickness tensile test of a sandwich panel. The supports upper and lower bonding blocks, which make up the equipment, have oscillating end. For attachment to the test machine, the fixings provided are standard connections type of DM ("male studs with diameter 0.50" 1.25 holes of ...
02
Upper and lower bonding blocks of the equipment are realized each with a double yoke arrangement. This conformation is made in order to allow full alignment of the sample during tensile load. On the testing machine there is an attachment standard 1.25" diameter male studs with 0.50" diameter cross-pin holes. ...
ASTM SRJ-D638 Testing Fixture Tensile tests measure the force required to break a plastic sample specimen and the extent to which the specimen stretches or elongates to that breaking point. ASTM D-638 tensile test procedure: Specimens are placed in the grips of the universal tester at a specified grip separation ...
ASTM D7269 Testing Fixture These test methods cover the tensile testing of aramid threads, twisted cables from these yarns and fabrics from these cables. The yarn or cord can be wound on cones, tubes, coils, chokes, or beams; It can be woven into fabric; or they can be realized in ...
ASTM D6415 Testing Fixture This fixture is useful to indicate the curved beam strength of a continuous fiber - reinforced composite material. For the test run it is necessary to use a curved beam sample 90 ° that has to be positioned for the four-point-bending test apparatus in order to ...
SPECIMEN FABBRICATION AIDS
01
To characterize the mechanical properties of the polymer to be used as the matrix material in a new composite material system it is often necessary. Thermoset polymer specimens can often be cast to finish dimensions in open molds.
BS EN 455-2 - Punch BS EN 455-2 describes the testing requirements for determination of physical properties, including break strength, before and after accelerated aging, of medical gloves for single use, surgical gloves, examination/procedure gloves, long-cuff medical gloves, and seemed/welded gloves. For this test, we recommend either pneumatic grips side ...
ASTM D638 A Testing Fixture The fixture was designed in relation to the test method expressed in ASTM D638 designation. This method has been realized to produce tensile properties data for the control and specification of the plastic materials. The collection of these data is useful for the qualitative characterization and ...
ASTM D638 Testing Fixture ASTM D638 tensile tests measure the force required to break a plastic sample specimen and the extent to which the specimen stretches or elongates to that breaking point. Tensile test procedure: Specimens are placed in the grips of the universal tester at a specified grip separation ...
TENSILE LOADING
TENSILE WEDGE GRIP INSERTS TESTING FIXTURE Wedge grip inserts of all types, in all sizes and load capacities to fit all existing wedge grip bodies, can be provided, including custom designs for special applications. While machined serration grip faces, either straight- or cross-serrated, are very popular, grip faces covered with ...
ASTM D897 Testing Fixture To help maintain the axial alignment load, usually universal joints are used in traction load applications. Can be designed and manufactured universal joints of all the final attack configurations and the load capacity. Usually, the material chosen for the realization of joints is 17-4 PH stainless ...
Sophia High Tech provides a wide range of tensile wedge grips to perform your testing. Elevated and reduced temperature tensile test procedures are available.Tensile tests measure the force required to break a plastic sample specimen and the extent to which the specimen stretches or elongates to that breaking point. Such ...
ASTM D882 TESTING FIXTURE In general, the thin sheet to be tested, plastic or metal film or sheeting up to 0.040 "in thickness, is held by the line of contact at each end between the flat reinforcing plates and the eccentric rolls. To facilitate the installation of the specimen cylinders ...
ASTM C307 TESTING FIXTURE The equipment is composed of lower and upper handles, which are equal. Its purpose is to determine the resistance to traction of briquettes special form of mortar, mortar and other similar materials of monolithic lining. The stop plates on the grips center the specimen fore and ...
Foam tests and foam testers provide a standard method of obtaining data for research and development, quality control, acceptance or rejection under specifications, and special purposes. Type A specimens are used when enough sample material exists to form the necessary specimen. Type B is preferred when smaller specimens are available, ...
07
To tensile test cordage, rope, flat strapping and similar flexible materials that might be otherwise difficult to grip without creating undesirable stress concentrations and premature failures, typically are used split capstan grips. Depending on your needs, it is possible to configure the capstan grips. To hold the sample, capstan grips …
ASTM D412 Testing Fixture This method covers the effect of the application of a tension load to vulcanized rubber and similar rubber-like material at room temperature and elevate temperature. Covered are tests for tensile stress, tensile strength, ultimate elongation and set. The method is not applicable to the testing of ...
ADAPTERS, LOCKS RINGS AND PINS Locking rings, adapters, and brooches of any configuration, to adapt specific test equipment to every type of mechanical or servo-hydraulic test machine. Every sistem can be customized according to Customer needs.